محصور کردن مواد آلی پودری گسترده در سیستم کپسول شیشه ای متمرکز برای بتن خود ترمیم

Encapsulation of expansive powder minerals within a concentric glass capsule system for self-healing concrete

سال انتشار : 2016

تعداد صفحه : 15

کلیدواژه ها: Powder mineral encapsulation, Expansion, Crack sealing, Strength recovery, Durability, Self-healing kinetics, Materials microstructure

 

   دانلود    سفارش ترجمه

ABSTRACT

This study presents the application of encapsulated expansive powder minerals (magnesium oxide, bentonite and quicklime) for self-healing of cement-based mortars. A system of concentric glass macrocapsules was used to envelope the expansive minerals (outer capsule) and water (inner capsule). Mortar samples containing concentric macrocapsules with different mineral combinations were cracked and healed under three different curing regimes; ambient conditions, high humidity exposure and immersed in water. Self-healing was assessed based on visual crack sealing, mechanical strength recovery and improvement in durability investigated by means of capillary sorption tests. Micro-structural analysis of the healing materials was investigated using FT-IR, XRD and SEM-EDX for exploring self-healing kinetics. Immersed in water have yielded the optimum healing efficiency with 95% crack sealing and 25% strength recovery in 28 days. Data showed an increasing trend in 56 days for both crack sealing and load recovery. The improvement in terms of capillary absorption of healed samples was also significant after 28 days of healing. Selfhealing kinetics revealed that the expansive minerals were hydrated in the initial healing period and slowly carbonated over time until the peripheral crack zone became adequately water tight.

زبان فایل

مجلات و ژورنال های بین المللی

Elsevier

ترجمه

نوع فایل

رایگان

سال انتشار

2016

دیدگاهها

هیچ دیدگاهی برای این محصول نوشته نشده است.

اولین نفری باشید که دیدگاهی را ارسال می کنید برای “محصور کردن مواد آلی پودری گسترده در سیستم کپسول شیشه ای متمرکز برای بتن خود ترمیم”

نشانی ایمیل شما منتشر نخواهد شد.